Opinions? Looks like a stock header with at T3 flange welded on it????
its not for me, but ...for those of you looking to build kit mabey.


http://cgi.ebay.com/ebaymotors/ws/eBayISAPI.dll?ViewItem&category=33742&item=7937067089&rd=1

I don't know if I would really trust that....come to think of it...

That sucker is strong as hell. I think it **might** make a good turbo header. Only problem would be the placement of the exhaust housing relative to the A/C compressor. You wouldn't have enough room for a DP to sneak by.

It's a stock exhaust manifold with a t3 flange.

i can almost hear the cracking now

Originally posted by turbo8u
i can almost hear the cracking now

That manifold will last about as long as this dog.

naw, the material is good. It's just the placement I would have a problem with.

I'd question the welds. Was it done with a high nickle content rod? Doubt it. Was the manifold cherry red when it was welded? I doubt that very much, too.

My stock manifold cracked to shit with NO weight on it. I don't think I would trust it with the weight of a turbo unless it was WELL braced.

Originally posted by Ducking_Fumbass
I'd question the welds. Was it done with a high nickle content rod? Doubt it. Was the manifold cherry red when it was welded? I doubt that very much, too. My stock manifold cracked to shit with NO weight on it. I don't think I would trust it with the weight of a turbo unless it was WELL braced.

Exaclty.....welding cast is no walk in the park and must be done by someone who has alot of experience with it. Cast can be welded with the right nickel rod and proper prep work but at that price i doubt it very much. Cast ends up being pre heated for 12 hours usually.

You would be buying one shitty paperweight there.


Terry

96 Eagle Talon ESI....Daily driver

97 Eclipse.........

why is it one consistent color? isnt that kinda strange?

Originally posted by 97whitESi
why is it one consistent color? isnt that kinda strange?

um how about PAINT